Product quality:

In line with oil and gas industry standard of the People's Republic of China (SY/T5504.6-2022 Evaluation method

for well cement additives-Part6: Light-weight additive)

技术指标 Technical indicator1：

技术指标 Technical indicator2：

漂珠类油井水泥减轻剂理化性能要求

加有减轻剂的低密度水泥浆性能要求

Physical and chemical performance requirements for floating bead type light-weight

additive for oil well cement

Performance requirements for low-density cement slurry with

light-weight additive

项目

项目

外观 具有流态的颗粒

1.60≤ρ<1.75

≤ 1.4

≤ 1.5

≥ 14.0

1.30≤ρ<1.60

≤ 1.4

≤ 2.0

≥ 7.0

ρ<1.30

≤ 1.4

≤ 2.5

≥ 3.5

≤ 0.5

≥ 80.0

≤ 8.0

≤ 0.80

≤ 0.05

指标

Index

不同密度水泥浆性能指标

Performance indicators of cement

slurry with different densities

Item

Item

Appearance

水泥浆密度，g/cm³

Cement slurry density

游离液，%

Free liquid

沉降稳定性，%

Settling stability

48h 抗压强度，MPa

48-hour compressive strength

Particles with a flow state

水分，%

Moisture content

漂浮率，%

Floatation ratio

细度（315μm 筛余），%

Fineness(315μm sieve residue)

密度，g/cm³

Density

耐压性能，g/cm³

pressure resistant performance

47

B油井水泥外加剂 Oil well cement admixtures

Function features:

Recommended dosage:

推荐加量：

功能特点：

Product packaging:

产品包装：

油气井用冲洗剂 烷基苯磺酸盐复合物 TW210L

Washing agent for oil-gas well - alkylbenzene

Sulfonate compound

(TW210L)

油气井用冲洗剂烷基苯磺酸盐复合物 TW210L 是我公司研制生产的一种低 ( 高 ) 温条件下使用的弱酸性

井壁专用清洗剂，以满足固井施工前对井壁的特殊要求。

TW210L 主要用于固井施工前，冲洗井壁附着的油基钻井泥浆、泥饼。

TW210L 是无色或浅黄色液体。

配制 1m 的 TW210L 工作液时，先加水 1/2 左右，再加入 TW210L 液体 50kg ～ 150kg，边加边搅拌，

待加足水搅拌均匀即可。

TW210L 工作液使用一段时间后，应适当添加 TW210L 或更换工作液。

1、使用温度在 90℃以上时，TW210L 液体加量按 5%；

2、使用温度在 80℃～ 90℃时，TW210L 液体加量按 10%；

3、使用温度在 70℃～ 80℃时，TW210L 液体加量按 12%；

4、使用温度在 50℃～ 70℃时，TW210L 液体加量按 15%。

TW210L 液体净重 20kg/ 桶，采用高密度聚乙烯塑料桶包装；

Washing agent for oil-gas well - alkylbenzene Sulfonate compound (TW210L) is a weakly-acidic well wall cleaning

agent developed and produced by our company for use in low (high) temperature conditions to meet the special

requirements of the well wall before cementing construction.

TW210L is mainly used to flush the oil-based drilling drilling fluid and drilling fluid cake attached to the well wall

before cementing construction.

TW210L is colorless or light-yellow liquid.

When preparing 1m³ TW210L working solution, about 1/2 water is added first, then 50kg~150kg TW210L liquid is

added and stirred, until enough water is added and stirred evenly.

After the TW210L working solution is used for a period of time, TW210L shall be appropriately added or the

working liquid replaced.

1. When the working temperature is above 90°C, the dosage of TW210L liquid is 5%;

2. When the working temperature is 80°C~90°C, the dosage of TW210L liquid is 10%;

3. When the working temperature is 70°C~80°C, tthe dosage of TW210L liquid is 12%;

4. When the working temperature is 50°C~70°C, the dosage of TW210L liquid is 15%;

The net weight of TW210L liquid is 20kg/drum, and high-density polyethylene plastic drum is adopted.

³

48 B油井水泥外加剂 Oil well cement admixtures

Product quality:

产品质量：

符合企业标准 Q/91510904MA66H91U2M·6—2023

符合中国石油化工集团公司企业标准 Q/SH CG0209-2023

In line with enterprise standard (Q/91510904MA66H91U2M·6-2023)

In line with enterprise standard of Sinopec Group (Q/SH CG0209-2023)

技术指标 Technical indicator1：

技术指标 Technical indicator2：

固井冲洗剂理化性能指标

固井冲洗液技术指标

Physical and chemical performance indicators of cementing flushing agent

Technical indicators of cementing flushing fluid

表观粘度，mPa·s

塑性粘度，mPa·s

外观

PH 值 6.0 ～ 9.0

0.80 ～ 1.05

≤ 15

≤ 10

≥ 85

指标

Index

指标

Index

项目

Item

项目

Item

Apparent viscosity

Plastic viscosity

冲洗效率 η(20 ℃ ± 2 ℃ )， %

Washing efficiency η(20°C ± 2°C)

Appearance

PH value

密度，g/cm³

Density

无色、均匀液体，无霉变

Colorless, uniform liquid without mildew

49

B油井水泥外加剂 Oil well cement admixtures

Function features:

Recommended dosage:

Product quality:

推荐加量：

产品质量：

功能特点：

油气井用隔离剂有机聚合物 TW220S 为棕灰色粉末，易分散于水中。

TW220S 配制成的粘性基液，具有优良的悬浮性和剪切稀释性，基液中加入加重剂配制成的加重隔离液能

有效隔离泥浆和水泥浆，提高对泥浆的顶替效率。

TW220S 干粉加量一般为水泥干重的 2.0 ～ 4.0%；

TW220S 干粉净重 25kg/ 袋，采用外层三合一牛皮纸复合袋或塑料编织袋，内层聚乙烯薄膜袋。

符合企业标准 Q/91510904MA66H91U2M·7—2023

符合中国石油化工集团公司企业标准 Q/SH CG0208-2023

Product packaging:

产品包装：

油气井用隔离剂 有机聚合物 TW220S

Spacer for oil-gas well - organic polymer

(TW220S)

Spacer for oil-gas well - organic polymer (TW220S) is brown-gray powder and easily dispersed in water.

The viscous base solution prepared by TW220S has excellent suspension property and shear dilution property.

The weighted separating solution prepared by adding weighting agent to the base solution can effectively isolate drilling

fluid and cement slurry and improve the displacement efficiency of drilling fluid.

The net weight of TW220S dry powder is 25kg/bag, the outer layer adopts 3-in-1 kraft paper composite bag or

plastic woven bag, and the inner layer adopts polyethylene film bag.

In line with enterprise standard (Q/91510904MA66H91U2M·7-2023)

In line with enterprise standard of Sinopec Group (Q/SH CG0208-2023)

The dosage of TW220S dry powder is generally 2.0~4.0% of the dry weight of cement;

50 B油井水泥外加剂 Oil well cement admixtures

技术指标 Technical indicator1：

隔离剂技术要求Technical requirements for spacer

隔离剂技术要求Technical requirements for spacer

指标

Index

指标

Index

项目

Item

项目

Item

外观

稠化时间之比

流动粉末

≥ 1

20 ～ 60

±0.05

Appearance

Ratio of thickening time

塑性粘度（常温），mPa·s

Plastic viscosity (normal temperature)

上、下密度差，g/cm³

Density difference between top and down

Flowing powder

技术指标 Technical indicator2：

51

B油井水泥外加剂 Oil well cement admixtures

Function features:

Recommended dosage:

Product quality:

推荐加量：

产品质量：

功能特点：

Product packaging:

产品包装：

油井水泥用降失水剂 丙烯酰胺基甲基丙磺酸共聚物 TW300L

Filtrate reducer for oil well cement -acrylamide methyl propyl sulfonic acid

copolymer

(TW300L)

油井水泥用降失水剂丙烯酰胺基甲基丙磺酸共聚物 TW300L 适用于套管、尾管注水泥和挤水泥作业，耐

高温，适用温度范围广。

TW300L 配制的水泥浆具有流变性好、滤失量很小、析水低，具有较好的防气窜作用。抗盐抗钙，最高抗

盐至饱和盐水。

TW300L 配制出的水泥浆体系稳定，一般只需另外加入少量分散剂。

TW300L 为无色至浅棕色粘稠液体；

TW300L 液体净重 25kg/ 桶或 1000kg/ 桶，采用高密度聚乙烯塑料桶包装；

符合中华人民共和国石油天然气行业标准 SY/T5504.2-2013 油井水泥外加剂评价方法第 2 部分：降失

水剂。

1.TW300L 液体用作淡水水泥浆降失水剂时，加量一般为 2.0 ～ 5.0％；

2.TW300L 液体用作盐水水泥浆降失水剂时，加量一般为 3.0 ～ 7.0％。

Filtrate reducer for oil well cement-acrylamide methyl propyl sulfonic acid copolymer (TW300L) is suitable for

cementing and cement squeezing operations of casing and tail pipe. They are resistant to high temperature and suitable

for a wide temperature range.

The cement slurry prepared by TW300L is featured by good rheological property, low filtrate loss, low water

seepage, and good anti-gas channeling effect. They are resistant to salt and calcium, up to saturated salt water.

The cement slurry system prepared by TW300L is stable, and generally only a small amount of dispersant needs to

be added.

TW300L is colorless to light-brown viscous liquid;

The net weight of TW300L liquid is 25kg/drum or 1000kg/drum, and high-density polyethylene plastic drum is

adopted.

In line with oil and gas industry standard of the People's Republic of China (SY/T5504.2-2013 Evaluation method

for well cement additives-Part 2: Fluid loss additive)

1. When TW300L liquid is used as fluid loss additive in fresh water cement slurry, the dosage is generally 2.0~5.0%;

2. When TW300L liquid is used as fluid loss additive in salt water cement slurry, the dosage is generally 3.0~7.0%.

52 B油井水泥外加剂 Oil well cement admixtures

技术指标 Technical indicator1：

油井水泥降失水剂物理性能要求

Physical performance requirements for Filtrate reducer

指标

Index

项目

Item

材料类别

Material category

液体类

Liquid

外观

Appearance

密度，g/cm³

Density

均匀无霉变

Uniform without mildew

基准密度 ±0.02

Reference density ±0.02

技术指标 Technical indicator2：

加有降失水剂的基准配方水泥浆性能要求

Performance requirements for benchmark formula cement slurry with added fluid

初始稠度，Bc

稠化线形突变值，Bc

过渡时间，min

失水量，mL

游离液，%

24h 抗压强度，MPa

≤ 30

≤ 10

≤ 40

≤ 150

≤ 1.4

≥ 14

指标

Index

项目

Item

Initial consistency

Sudden change value of thickening-time

Transition time

Fluid loss

Free liquid

24-hour compressive strength

53

B油井水泥外加剂 Oil well cement admixtures

Function features:

Recommended dosage:

Product quality:

推荐加量：

产品质量：

功能特点：

Product packaging:

产品包装：

油井水泥用降失水剂 丙烯酰胺基甲基丙磺酸共聚物 TW300S

Filtrate reducer for oil well cement - acrylamide methyl propyl sulfonic acid

copolymer

(TW300S)

油井水泥用降失水剂丙烯酰胺基甲基丙磺酸共聚物 TW300S 适用于套管、尾管注水泥和挤水泥作业，耐

高温，适用温度范围广。

TW300S 配制的水泥浆具有流变性好、滤失量很小、析水低，具有较好的防气窜作用。抗盐抗钙，最高抗

盐至饱和盐水。

TW300S 配制出的水泥浆体系稳定，一般只需另外加入少量分散剂。

TW300S 为浅棕灰色粉末和颗粒。

TW300S 干粉净重 25kg/ 袋，采用外层三合一牛皮纸复合袋或塑料编织袋，内层聚乙烯薄膜袋。

符合中华人民共和国石油天然气行业标准 SY/T5504.2-2013 油井水泥外加剂评价方法第 2 部分：降失

水剂。

1.TW300S 干粉用作淡水水泥浆降失水剂时，加量一般为 2.0 ～ 3.0％；

2.TW300S 干粉用作盐水水泥浆降失水剂时，加量一般为 2.0 ～ 4.0％。

Filtrate reducer for oil well cement-acrylamide methyl propyl sulfonic acid copolymer (TW300S) is suitable for

cementing and cement squeezing operations of casing and tail pipe. They are resistant to high temperature and suitable

for a wide temperature range.

The cement slurry prepared by TW300S is featured by good rheological property, low filtrate loss, low water

seepage, and good anti-gas channeling effect. They are resistant to salt and calcium, up to saturated salt water.

The cement slurry system prepared by TW300S is stable, and generally only a small amount of dispersant needs to

be added.

TW300S is light brown-gray powder and particle.

The net weight of TW300S dry powder is 25kg/bag, the outer layer adopts 3-in-1 kraft paper composite bag or

plastic woven bag, and the inner layer adopts polyethylene film bag.

In line with oil and gas industry standard of the People's Republic of China (SY/T5504.2-2013 Evaluation method

for well cement additives-Part 2: Fluid loss additive)

1.When TW300S dry powder is used as fluid loss additive in fresh water cement slurry, the dosage is generally

2.0~3.0%;

2.When TW300S dry powder is used as fluid loss additive in salt water cement slurry, the dosage is generally

2.0~4.0%.

54 B油井水泥外加剂 Oil well cement admixtures

技术指标 Technical indicator1：

油井水泥降失水剂物理性能要求

指标

Index

项目

Item

外观

材料类别

固体类

水分，%

细度（0.315mm筛余），%

≤ 8

≤ 15

Appearance

Material category

Solid

密度，g/cm³

Density

Moisture content

Fineness(0.315mm sieve residue)

无受潮板结

No moisture hardening

基准密度 ±0.02

Reference density ±0.02

Physical performance requirements for Filtrate reducer

加有降失水剂的基准配方水泥浆性能要求

指标

Index

项目

Item

≤ 30

≤ 10

≤ 40

≤ 150

≤ 1.4

≥ 14

初始稠度，Bc

稠化线形突变值，Bc

过渡时间，min

失水量，mL

游离液，%

24h 抗压强度，MPa

Initial consistency

Sudden change value of thickening-time

Transition time

Fluid loss

Free liquid

24-hour compressive strength

Performance requirements for benchmark formula cement slurry with added fluid

技术指标 Technical indicator2：

55

B油井水泥外加剂 Oil well cement admixtures

油井水泥用降失水剂 改性纤维素复合物 TW310S

Filtrate reducer for oil well cement - modified

cellulose compound

(TW310S)

Function features:

Recommended dosage:

Product quality:

推荐加量：

产品质量：

功能特点：

Product packaging:

产品包装：

油井水泥用降失水剂改性纤维素复合物 TW310S 适用于套管、尾管注水泥和挤水泥作业。

TW310S 加入水泥后能有效降低水泥浆的滤失量，减小或消除自由水，对水泥石早期强度无不良影响，并

具有一定的抗钙、抗盐和防气窜作用。

TW310S 一般应与 SXY 减阻剂配伍使用，发挥协同效能，同时可在不加缓凝剂的条件下，灵活调节稠化

时间。

TW310S 已在国内很多油田的固井施工中大面积推广应用，均获得很好的效果。TW310S 尤其适用于大

斜度及水平井注水泥。

TW310S 为灰褐色粉末和颗粒。

TW310S 干粉加量一般为水泥干重的 0.8 ～ 2.0%；

TW310S 干粉净重 25kg/ 袋，采用外层三合一牛皮纸复合袋或塑料编织袋，内层聚乙烯薄膜袋。

符合中华人民共和国石油天然气行业标准 SY/T5504.2-2013 油井水泥外加剂评价方法第 2 部分：降失

水剂。

Filtrate reducer for oil well cement - modified cellulose compound (TW310S) is suitable for cementing and cement

squeezing operations of casing and tail pipe.

After TW310S is added to cement, it can effectively reduce the filtrate loss of cement slurry, reduce or eliminate

free water; it has no adverse effect on the early strength of cement, and have certain anti-calcium, anti-salt and anti-gas

channeling effects.

TW310S shall generally be used with SXY drag reducer to achieve synergistic effect; it can also flexibly adjust the

thickening time without the addition of retarder.

TW310S has been widely applied to cementing construction in many domestic oilfields, and good results have been

obtained. TW310S is especially suitable for cementing for high-slope and horizontal wells.

TW310S is grayish-brown powder and particle.

The dosage of TW310S dry powder is generally 0.8~2.0% of the dry weight of cement;

The net weight of TW310S dry powder is 25kg/bag, the outer layer adopts 3-in-1 kraft paper composite bag or

plastic woven bag, and the inner layer adopts polyethylene film bag.

In line with oil and gas industry standard of the People's Republic of China (SY/T5504.2-2013 Evaluation method

for well cement additives-Part 2: Fluid loss additive)

56 B油井水泥外加剂 Oil well cement admixtures

技术指标 Technical indicator1：

油井水泥降失水剂物理性能要求

指标

Index

项目

Item

外观

材料类别

固体类

水分，%

细度（0.315mm筛余），%

无受潮板结

基准密度 ±0.02

≤ 8

≤ 15

Appearance

Material category

Solid

密度，g/cm³

Density

Moisture content

Fineness(0.315mm sieve residue)

No moisture hardening

Reference density ±0.02

Physical performance requirements for Filtrate reducer

加有降失水剂的基准配方水泥浆性能要求

指标

Index

项目

Item

≤ 30

≤ 10

≤ 40

≤ 150

≤ 1.4

≥ 14

初始稠度，Bc

稠化线形突变值，Bc

失水量，mL

24h 抗压强度，MPa

Initial consistency

Sudden change value of thickening-time

过渡时间，min

Transition time

Fluid loss

游离液，%

Free liquid

24-hour compressive strength

Performance requirements for benchmark formula cement slurry with added fluid

技术指标 Technical indicator2：

57

B油井水泥外加剂 Oil well cement admixtures

Function features:

功能特点：

油井水泥降失水剂 改性聚乙烯醇 TW320L

Filtrate reducer for oil well cement - modified

polyvinyl alcohol

(TW320L)

油井水泥降失水剂改性聚乙烯醇 TW320L 适用于套管、尾管注水泥和挤水泥作业，可用于循环温度

30 ～ 90℃的井深。

TW320L 配制的水泥浆具有流变性好、滤失量小、析水率低、低温下早期强度高、水泥石弹性好、渗透率

低，且有一定的防气窜能力等特点，是低温浅井注水泥的理想降滤失剂。

TW320L 和早强剂（TW130S）、减阻剂（TW150S）、硅灰以及漂珠等减轻材料配制的硅灰—低密度

水泥浆体系已成功地应用于许多油田的低温低压油层的固井施工中。

TW320L 可以与 TW150S 减阻剂配用，以调节水泥浆的流变性能和稠化时间。

TW320L 为棕色粘稠液体；

Filtrate reducer for oil well cement - modified polyvinyl alcohol (TW320L) is suitable for cementing and cement

squeezing operations of casing and tail pipe, and can be used in deep wells with circulating temperature of 30~90°C.

The cement slurry prepared by TW320L is featured by good rheological property, low filtrate loss, low water

seepage, high early strength at low temperature, good elasticity of cement block, low permeability, and certain anti-gas

channeling ability. It is an ideal filtrate loss reducer for low-temperature shallow well cementing.

The silica fume-low density cement slurry system composed of TW320L, fast-hardening agent (TW130S),

drag reducer (TW150S), silica fume, cenosphere and other lightening materials has been successfully applied to the

cementing construction of low temperature and low pressure reservoir in many oilfields.

TW320L can be used with TW150S drag reducer to adjust the rheological property and thickening time of cement

slurry.

TW320L a brown viscous liquid;

Recommended dosage:

推荐加量：

Product packaging:

产品包装：

TW320L 液体加量一般为水泥干重的 4.0 ～ 6.0%；

TW320L 液体净重 25kg/ 桶，采用高密度聚乙烯塑料桶包装；

The dosage of TW320L liquid is generally 4.0~6.0% of the dry weight of cement;

The net weight of TW320L liquid is 25kg/drum, and high-density polyethylene plastic drum is adopted.

Product quality:

产品质量：

符合中华人民共和国石油天然气行业标准 SY/T5504.2-2013 油井水泥外加剂评价方法第 2 部分：降失

水剂。

In line with oil and gas industry standard of the People's Republic of China (SY/T5504.2-2013 Evaluation method

for well cement additives-Part 2: Fluid loss additive)

58 B油井水泥外加剂 Oil well cement admixtures

技术指标 Technical indicator1：

油井水泥降失水剂物理性能要求

Physical performance requirements for Filtrate reducer

材料类别 指标

Index

项目

Material category Item

³

外观

密度，g/cm

液体类

Liquid

Appearance

Density

均匀无霉变

Uniform without mildew

基准密度 ±0.02

Reference density ±0.02

技术指标 Technical indicator2：

加有降失水剂的基准配方水泥浆性能要求

Performance requirements for benchmark formula cement slurry with added fluid

初始稠度，Bc

稠化线形突变值，Bc

过渡时间，min

失水量，mL

游离液，%

24h 抗压强度，MPa

≤ 30

≤ 10

≤ 40

≤ 150

≤ 1.4

≥ 14

指标

Index

项目

Item

Initial consistency

Sudden change value of thickening-time

Transition time

Fluid loss

Free liquid

24-hour compressive strength

59

B油井水泥外加剂 Oil well cement admixtures

Function features:

功能特点：

油井水泥降失水剂 聚乙烯醇复合物 TW320S

Filtrate reducer for oil well cement - polyvinyl

alcohol compound

(TW320S)

油井水泥降失水剂聚乙烯醇复合物 TW320S 适用于套管、尾管注水泥和挤水泥作业，可用于循环温度

35 ～ 100℃的井深（与 TW700L、TW710L 等缓凝剂配合使用）。

TW320S 配制的水泥浆具有流变性好、滤失量很小、析水率低、低温下早期强度高、水泥浆在界面处形成

不渗透膜，故有较好的防气窜能力等特点。

TW320S 对水泥浆的流动性能和稠化时间几乎不产生影响。

TW320S 是一种干粉材料，必须与水泥干混使用。

TW320S 可以与 TW150S 减阻剂配用，以调节水泥浆的流变性能和稠化时间。

TW320S 为浅棕灰色粉末和颗粒。

Filtrate reducer for oil well cement - polyvinyl alcohol compound (TW320S) is suitable for cementing and cement

squeezing operations of casing and tail pipe, and can be used in deep wells with circulating temperature of 35~100°C

(together with TW700L, TW710L and other retarders).

The cement slurry prepared by TW320S is featured by good rheological property, low filtrate loss, low water

seepage and high early strength at low temperature, and can form an impermeable film at the interface to achieve good

anti-gas channeling effect.

TW320S has little effect on the rheological property and thickening time of cement slurry.

TW320S is a dry powder material that must be dry mixed with cement.

TW320S can be used with TW150S drag reducer to adjust the rheological property and thickening time of cement

slurry.

TW320S is light brown-gray powder and particle.

Recommended dosage:

推荐加量：

Product packaging:

产品包装：

TW320S 干粉加量一般为水泥干重的 1.8 ～ 2.5%；

TW320S 干粉净重 25kg/ 袋，采用外层三合一牛皮纸复合袋或塑料编织袋，内层聚乙烯薄膜袋。

The dosage of TW320S dry powder is generally 1.8~2.5% of the dry weight of cement;

The net weight of TW320S dry powder is 25kg/bag, the outer layer adopts 3-in-1 kraft paper composite bag or

plastic woven bag, and the inner layer adopts polyethylene film bag.

Product quality:

产品质量：

符合中华人民共和国石油天然气行业标准 SY/T5504.2-2013 油井水泥外加剂评价方法第 2 部分：降失

水剂。

In line with oil and gas industry standard of the People's Republic of China (SY/T5504.2-2013 Evaluation method

for well cement additives-Part 2: Fluid loss additive)

60 B油井水泥外加剂 Oil well cement admixtures

技术指标 Technical indicator1：

油井水泥降失水剂物理性能要求

指标

Index

项目

Item

外观

材料类别

固体类

水分，%

细度（0.315mm筛余），%

无受潮板结

基准密度 ±0.02

≤ 8

≤ 15

Appearance

Material category

Solid

密度，g/cm³

Density

Moisture content

Fineness(0.315mm sieve residue)

No moisture hardening

Reference density ±0.02

Physical performance requirements for Filtrate reducer

加有降失水剂的基准配方水泥浆性能要求

指标

Index

项目

Item

≤ 30

≤ 10

≤ 40

≤ 150

≤ 1.4

≥ 14

初始稠度，Bc

稠化线形突变值，Bc

过渡时间，min

失水量，mL

游离液，%

24h 抗压强度，MPa

Initial consistency

Sudden change value of thickening-time

Transition time

Fluid loss

Free liquid

24-hour compressive strength

Performance requirements for benchmark formula cement slurry with added fluid

技术指标 Technical indicator2：

61

B油井水泥外加剂 Oil well cement admixtures

油井水泥外加剂 改性丁苯胶乳 TW400L

Oil well cement admixture - modified styrene-butadiene latex

(TW400L)

Function features:

Recommended dosage:

Product quality:

推荐加量：

产品质量：

功能特点：

Product packaging:

产品包装：

油井水泥外加剂改性丁苯胶乳 TW400L 是一种改性丁苯胶乳，在生产制造过程中加入了高浓度的表面活

性剂和分散剂，以防止发生水泥浆的絮凝和闪凝。

掺加 TW400L 的胶乳水泥浆具有低失水、流变性好、防窜、高韧性等特点，可适用于高压油气井、小井眼、

侧钻井和分枝井固井。由于胶乳中的表面活性剂等在水泥浆混配中会产生大量的泡沫，因此在使用中需加入有

效的消泡剂。

TW400L 为乳白色液体。胶乳水泥浆体系主要由胶乳 TW400L、减阻剂 TW150S、消泡剂 TW110L 等

组成，各材料应同时应用。

TW400L 液体加量一般为水泥干重的 5.0 ～ 15.0%。

TW400L 液体净重 25kg/ 桶，采用高密度聚乙烯塑料桶包装。

符合企业标准 Q/91510904MA66H91U2M·22—2023

Oil well cement admixture - modified styrene-butadiene latex (TW400L) is a modified styrene butadiene latex, in

the manufacturing process, high-concentration surfactants and dispersants are added to prevent the flocculation and

flash coagulation of cement slurry.

The latex cement slurry mixed with TW400L is featured by low water loss, good rheological property, antichanneling, high toughness, etc. It can be applied to cementing of high-pressure oil and gas wells, small borehole,

sidetracking well and lateral wells. Because the surfactant in latex will produce a lot of foam in the mixing of cement

slurry, effective defoaming agents need to be added before use.

TW400L is milky liquid.Latex cement slurry system is mainly composed of latex TW400L, drag reducer TW150S,

defoaming agent TW110L. All such materials shall be applied at the same time.

The dosage of TW400L liquid is generally 5.0~15.0% of the dry weight of cement.

The net weight of TW400L liquid is 25kg/drum, and high-density polyethylene plastic drum is adopted.

In line with enterprise standard (Q/91510904MA66H91U2M·22-2023)

62 B油井水泥外加剂 Oil well cement admixtures

技术指标 Technical indicator:

≥ 14

≤ 10

≤ 40

≤ 1.4

≤ 30

指标

Index

项目

Item

抗压强度，MPa

compressive strength

稠化线形突变值，Bc

Sudden change value of thickening-time

过渡时间，min

Transition time

游离液，%

Free liquid

初始稠度，Bc

Initial consistency

63

B油井水泥外加剂 Oil well cement admixtures

油井水泥用防漏外掺料 改性玻璃纤维 TW500S

Leak-proof admixture for oil well cement - modified

glass fibre

(TW500S)

Function features:

Recommended dosage:

Product quality:

推荐加量：

产品质量：

功能特点：

Product packaging:

产品包装：

油井水泥用防漏外掺料改性玻璃纤维 TW500S 是为解决固井注水泥作业水泥浆漏失问题而设计开发的一

种专用惰性堵漏材料。

TW500S为白色或浅黄色纤维集束。TW500S在水泥浆中易于分散，在裂缝性漏失地层处能迅速形成桥堵，

防止水泥浆向地层进一步漏失的产生。TW500S 产品中的特种纤维材料经表面处理，对水泥有很好的亲和性，

有利于增加水泥石韧性，提高水泥环的抗冲击能力。TW500S 在国内油田固井施工中已取得显著效果。

TW500S 纤维加量一般为水泥干重的 0.3 ～ 0.5%。

TW500S 纤维直接均匀加入到水泥浆过渡 ( 混合 ) 罐中即可。

TW500S 纤维净重 25kg/ 桶，采用内层聚乙烯薄膜袋，外包装为铁桶或高密度聚乙烯塑料桶。

符合企业标准 Q/91510904MA66H91U2M·5—2023

Leak-proof admixture for oil well cement - modified glass fibre (TW500S) is a special inert plugging material

designed and developed to solve the problem of cement slurry leakage in cementing operation.

TW500S is cluster of white or light-yellow fiber.TW500S is easy to disperse in cement slurry, and can quickly

form a bridge plug at the fractured leakage formation to prevent further leakage of cement slurry to the formation.The

special fiber material in TW500S product has a good affinity for cement after surface treatment, which is conducive to

increasing the toughness of cement block and improving the impact resistance of cement ring.TW500S has achieved

remarkable results in cementing construction of domestic oilfields.

The dosage of TW500S fibre is generally 0.3~0.5% of the dry weight of cement.

TW500S fibre can be evenly added directly to the cement slurry transition

(mixing) tank.

The net weight of TW500S fibre is 25kg/drum,, the outer layer adopts metal drum or high-density polyethylene

plastic drum, and the inner layer adopts polyethylene film bag.

In line with enterprise standard (Q/91510904MA66H91U2M·5-2023)

64 B油井水泥外加剂 Oil well cement admixtures

技术指标 Technical indicator:

3～ 15

≤ 100

≥ 14

≤ 10

≥ 90

≤ 1.4

0.5～ 1.0

指标

Index

项目

Item

长度，mm

Length

漏失量，mL

Leakage amount

抗压强度，MPa

compressive strength

稠化线形突变值，Bc

Sudden change value of thickening-time

过渡时间，min

Transition time

游离液，%

Free liquid

稠化时间之比（60℃，32.8 MPa，37min）

Ratio of thickening time

65

B油井水泥外加剂 Oil well cement admixtures

Function features:

Recommended dosage:

Product quality:

推荐加量：

产品质量：

功能特点：

Product packaging:

产品包装：

油井水泥用中温缓凝剂 有机磷酸盐复合物 TW700L

Medium-temperature retarder for oil well cement - organic phosphate

compound

(TW700L)

油井水泥用中温缓凝剂有机磷酸盐复合物 TW700L 主要用于石油天然气钻探开发工程中套管、尾管注水

泥和挤水泥作业。

TW700L 适用于循环温度 90℃以下的井深。常规加量约占水泥干重的 0.05 ～ 0.5%，稠化时间 2 ～ 6

小时可调。

用 TW700L 配制的水泥浆具有流变性好、调凝作用单调、后期强度发展快、与其它常用外加剂配伍性好

等特点。

TW700L 黄色或棕黄色液体，施工时适宜配水使用。

根据稠化时间的实际要求，TW700L 液体加量一般为水泥干重的 0.05 ～ 0.5%。

TW700L 液体净重 25kg/ 桶，采用高密度聚乙烯塑料桶包装。

符合中华人民共和国石油天然气行业标准 SY/T5504.1-2013油井水泥外加剂评价方法第 1部分：缓凝剂。

Medium-temperature retarder for oil well cement - organic phosphate compound (TW700L) is mainly used for

cementing and cement squeezing operations of casing and tail pipe in oil and gas drilling and development projects.

The TW700L is suitable for deep well with circulating temperature below 90°C. The conventional dosage is about

0.05~0.5% of the dry weight of cement, and the thickening time is adjustable from 2 to 6 hours.

The cement slurry prepared by TW700L is featured by good rheological property, monotonic setting effect, rapid

development of strength in later period, and good compatibility with other commonly used admixtures.

TW700L is yellow or brownish-yellow liquid and should be used with water during construction.

According to the actual requirements for thickening time, The dosage of TW700L liquid is generally 0.05~0.5% of

the dry weight of cement.

The net weight of TW700L liquid is 25kg/drum, and high-density polyethylene plastic drum is adopted.

In line with oil and gas industry standard of the People's Republic of China (SY/T5504.1-2013 Evaluation method

for well cement additives-Part 1: Retarder).

66 B油井水泥外加剂 Oil well cement admixtures

技术指标 Technical indicator1：

油井水泥缓凝剂物理性能要求

Physical property requirements for retarder of oil well cement

材料类别 项目 指标

Material category Item Index

³

液体类

外观

密度，g/cm

均匀无霉变

Liquid 基准密度 ±0.02

Appearance

Density

Uniform without mildew

Reference density ±0.02

技术指标 Technical indicator2：

加有缓凝剂的基准配方水泥浆性能要求

Performance requirements for reference-formula cement slurry with retarder

≤ 30

≤ 10

≥ 60

≤ 25

≤ 20

≤ 40

≤ 1.4

≥ 14

指标

Index

项目

Item

初始稠度，Bc

Initial consistency

稠化线形突变值，Bc

Sudden change value of thickening-time

稠化时间延长值，min

Extension value of thickening time

加量敏感度，%

Dosage sensitivity

温度敏感度，%

Temperature sensitivity

过渡时间，min

Transition time

游离液，%

Free liquid

24h 抗压强度，MPa

24-hour compressive strength

67

B油井水泥外加剂 Oil well cement admixtures

Function features:

Recommended dosage:

Product quality:

推荐加量：

产品质量：

功能特点：

Product packaging:

产品包装：

油井水泥用高温缓凝剂 葡萄糖酸钠纤维素复合物 TW710L

High-temperature retarder for oil well cement - sodium gluconate cellulose

compound

(TW710L)

油井水泥用高温缓凝剂葡萄糖酸钠纤维素复合物 TW710L 主要用于石油天然气钻探开发工程中套管、尾

管注水泥和挤水泥作业。

TW710L 适用于循环温度 80 ～ 150℃的井深，稠化时间 3 ～ 6 小时可调。

TW710L 配制的水泥浆具有流变性好、析水率低、调凝效果明显、后期强度发展快、与其它常用外加剂配

伍性好等特点，并且有一定的滤失控制能力。

TW710L 为棕褐色粘性液体，施工时适宜配水使用。

TW710L 是有机物类高温缓凝剂，使用时较小的掺量，即能起到较强的缓凝效果；

TW710L 液体净重 25kg/ 桶，采用高密度聚乙烯塑料桶包装。

符合中华人民共和国石油天然气行业标准 SY/T5504.1-2013油井水泥外加剂评价方法第 1部分：缓凝剂。

根据稠化时间的实际要求，TW710L 液体加量一般为水泥干重的 0.1 ～ 1.0%。

High-temperature retarder for oil well cement - sodium gluconate cellulose compound (TW710L)is mainly used for

cementing and cement squeezing operations of casing and tail pipe in oil and gas drilling and development projects.

TW710L is suitable for deep well with circulating temperature of 80~150°C, and the thickening time is adjustable

from 3 to 6 hours.

The cement slurry prepared by TW710L is featured by good rheological property, low water seepage, obvious

setting effect, rapid development of strength in later period, and good compatibility with other commonly used

admixtures. It also has a certain filtrate loss control ability.

TW710L is brown viscous liquid and should be used with water during construction.

TW710L is an organic high-temperature retarder, a small dosage can achieve strong retarding effect.

The net weight of TW710L liquid is 25kg/drum, and high-density polyethylene plastic drum is adopted.

In line with oil and gas industry standard of the People's Republic of China (SY/T5504.1-2013 Evaluation method

for well cement additives-Part 1: Retarder).

According to the actual requirements for thickening time, The dosage of TW710L liquid is generally 0.1~1.0% of

the dry weight of cement.

68 B油井水泥外加剂 Oil well cement admixtures

技术指标 Technical indicator1：

油井水泥缓凝剂物理性能要求

Physical property requirements for retarder of oil well cement

指标

Index

项目

Item

材料类别

Material category

液体类

外观

Liquid

Appearance

密度，g/cm³

Density

均匀无霉变

Uniform without mildew

基准密度 ±0.02

Reference density ±0.02

技术指标 Technical indicator2：

加有缓凝剂的基准配方水泥浆性能要求

Performance requirements for reference-formula cement slurry with retarder

≤ 30

≤ 10

≥ 60

≤ 25

≤ 20

≤ 40

≤ 1.4

≥ 14

指标

Index

项目

Item

初始稠度，Bc

Initial consistency

稠化线形突变值，Bc

Sudden change value of thickening-time

稠化时间延长值，min

Extension value of thickening time

加量敏感度，%

Dosage sensitivity

温度敏感度，%

Temperature sensitivity

过渡时间，min

Transition time

游离液，%

Free liquid

24h 抗压强度，MPa

24-hour compressive strength

69

B油井水泥外加剂 Oil well cement admixtures

Function features:

Recommended dosage:

Product quality:

推荐加量：

产品质量：

功能特点：

Product packaging:

产品包装：

油井水泥用高温缓凝剂 羧基膦酸盐复合物 HT-R

High-temperature retarder for oil well cement - Carboxyphosphonates

compound

(HT-R)

油井水泥用高温缓凝剂 羧基膦酸盐复合物 HT-R 主要用于石油天然气钻探开发工程中套管、尾管注水泥

和挤水泥作业。

HT-R 适用于循环温度 80 ～ 150℃的井深，稠化时间 3 ～ 6 小时可调。

HT-R 配制的水泥浆具有流变性好、析水率低、调凝效果明显、后期强度发展快、与其它常用外加剂配伍

性好等特点，并且有一定的滤失控制能力。

HT-R 为棕红色液体，水溶性好。

HT-R 是聚合物类高温缓凝剂，虽然使用时掺量较大，但对油井水泥的适应性强，与其他水泥外加剂配伍

性更好，掺量与稠化时间线性关系很好。

HT-R 液体净重 20kg/ 桶或 1000kg/ 桶，采用高密度聚乙烯塑料桶包装。

符合中华人民共和国石油天然气行业标准 SY/T5504.1-2013油井水泥外加剂评价方法第 1部分：缓凝剂。

根据稠化时间的实际要求，HT-R 液体加量一般为水泥干重的 3.0 ～ 5.0%。

High-temperature retarder for oil well cement - Carboxyphosphonates compound(HT-R) is mainly used for

cementing and cement squeezing operations of casing and tail pipe in oil and gas drilling and development projects.

HT-R is suitable for deep well with circulating temperature of 80~150°C, and the thickening time is adjustable

from 3 to 6 hours.

The cement slurry prepared by HT-R is featured by good rheological property, low water seepage, obvious setting

effect, rapid development of strength in later period, and good compatibility with other commonly used admixtures. It

also has a certain filtrate loss control ability.

HT-R is brown-red liquid with good water solubility.

HT-R is a polymer-type high-temperature retarder. Although the dosage is large when using, it has strong

adaptability to oil well cement and better compatibility with other cement admixtures; the linear relationship between

the dosage and thickening time is very good.

The net weight of HT-R liquid is 20kg/drum or 1000kg/drum, and high-density polyethylene plastic drum is

adopted.

In line with oil and gas industry standard of the People's Republic of China (SY/T5504.1-2013 Evaluation method

for well cement additives-Part 1: Retarder).

According to the actual requirements for thickening time, The dosage of HT-R liquid is generally 3.0~5.0% of the

dry weight of cement.

70 B油井水泥外加剂 Oil well cement admixtures

技术指标 Technical indicator1：

油井水泥缓凝剂物理性能要求

Physical property requirements for retarder of oil well cement

指标

Index

项目

Item

材料类别

Material category

液体类

外观 均匀无霉变

Liquid

Appearance

密度，g/cm³

Density

Uniform without mildew

基准密度 ±0.02

Reference density ±0.02

技术指标 Technical indicator2：

加有缓凝剂的基准配方水泥浆性能要求

Performance requirements for reference-formula cement slurry with retarder

初始稠度，Bc

稠化线形突变值，Bc

稠化时间延长值，min

过渡时间，min

≤ 30

≤ 10

≥ 60

≤ 25

≤ 20

≤ 40

≤ 1.4

≥ 14

指标

Index

项目

Item

Initial consistency

Sudden change value of thickening-time

Extension value of thickening time

加量敏感度，%

Dosage sensitivity

温度敏感度，%

Temperature sensitivity

Transition time

游离液，%

Free liquid

24h 抗压强度，MPa

24-hour compressive strength

71

B油井水泥外加剂 Oil well cement admixtures

Function features:

Product quality:

产品质量：

功能特点：

Product packaging:

产品包装：

栲 胶

Tannin extracts

栲胶由富含单宁的树皮、果壳、果实、叶和木材等植物原料经水浸提、浓缩、干燥等工序制得的产品。

栲胶通常为棕黄色至棕褐色粉末状。栲胶主要用于鞣皮，制革业上称为植物鞣剂。栲胶可用作选矿抑制剂、

锅炉水处理剂、钻井泥浆稀释剂、金属表面防蚀剂等。栲胶还用于医药化工化学品、沥青混泥土添加剂、木工

胶粘剂等。

四川拓旺科技有限公司的前身是 1958 年成立的国有企业——成都栲胶厂。栲胶产品生产历史悠久，质量

保证。公司现有大量栲胶产品：杨梅栲胶、落叶松栲胶、橡椀栲胶等。

栲胶干粉净重 25kg/ 袋，采用外层三合一牛皮纸复合袋或塑料编织袋，内层聚乙烯薄膜袋。

符合中华人民共和国林业行业标准 LY/T1087-2021。

Tannin extracts is made from tannin-rich bark, fruit shell, fruit, leaf and wood by water extraction, concentration,

drying and other processes.

Tannin extracts is usually brown-yellow to brown powder. Tannin extract is mainly used for tanning, and is

called vegetable tanning agent in tanning industry. Tannin extract can be used as mineral dressing inhibitor, boiler

water treatment agent, drilling fluid thinner, metal surface corrosion inhibitor, etc. Tannin extract is also used in

pharmaceutical chemicals, asphalt cement additives, woodworking adhesives, etc.

The predecessor of Sichuan Tuowang Technology Co., Ltd. is Chengdu Tannin Extract Plant, a state-owned

enterprise founded in 1958. With a long history of production of tannin extract products, the quality can be ensured.

Currently, the Company provides various tannin extract products: myrtle tannin extract, larch tannin extract, valonia

tannin extract, etc.

The net weight of Tannin extract dry powder is 25kg/bag, the outer layer adopts 3-in-1 kraft paper composite bag

or plastic woven bag, and the inner layer adopts polyethylene film bag.

In line with the forestry industry standard of the People's Republic of China (LY/T1087-2021)

72 C 林产化学品 Forest chemicalsadmixtures

技术指标 Technical indicator：

杨梅栲胶技术指标Technical indicators of myrtle tannin extract

水分，%

单宁，%

沉淀，%

PH 值

≤ 12.0

≤ 4.0

≤ 69.0

≤ 2.0

4.5 ～ 5.5

≤ 10.0

≤ 12.0

≤ 5.0

≤ 67.0

≤ 4.0

4.5 ～ 5.5

≤ 16.0

≤ 12.0

≤ 6.0

≤ 65.0

≤ 6.0

4.5 ～ 5.5

≤ 26.0

指标名称

Indicator name

外观

Appearance

Moisture content

不溶物，%

Insoluble substance

Tannin

Sediment

PH value

总颜色

Total color

优等品

Superior product

淡棕黄色至棕黄色粉末

Light brown-yellow to brown-yellow powder

一等品

First-class product

合格品

Qualified product

橡椀栲胶技术指标 Technical indicators of valonia extract

指标名称

冷溶 热熔

外观

水分，%

不溶物，%

单宁，%

沉淀，%

PH 值

总颜色

≤ 12.0

≤ 2.0

≤ 2.0

3.3 ～ 4.0

≤ 20.0

3.3 ～ 4.0

≤ 28.0

3.3 ～ 4.0

≤ 38.0

3.3 ～ 3.8 3.3 ～ 3.8

≤ 3.0 ≤ 5.0 ≤ 6.0 ≤ 8.0

≤ 68.0

≤ 2.5

≤ 66.0

≤ 3.5

≤ 62.0

≤ 3.5

≤ 70.0

≤ 4.0

≤ 66.0

≤ 12.0 ≤ 12.0 ≤ 12.0 ≤ 12.0

淡棕黄色至棕黄色粉末

Indicator name

Cold solubility Hot solubility

Appearance

Moisture content

Insoluble substance

Tannin

Sediment

PH value

Total color

优等品

Superior

product

Light brown-yellow to brown-yellow powder

一等品

First-class

product

一等品

First-class

product

合格品

Qualified

product

合格品

Qualified

product

73

C 林产化学品 Forest chemicalsadmixtures

磺化酚醛树脂配套检测试剂Ⅰ

Sulfonated methyl phenol-fomaldehyde resin matching detection reagent I

74 D 检测试剂 Test reagents

磺化酚醛树脂配套检测试剂Ⅱ

Sulfonated methyl phenol-fomaldehyde resin matching detection reagent II

75

D 检测试剂 Test reagents

混凝土高效外加剂

Concrete high-efficiency admixtures

FDT 系列混凝土高效外加剂是一种新型高效外加剂，已通过四川省建设委员会审查，并取得《四川省建设

系统新产品新技术推广许可证书》（证书编号：98016）。

FDT 系列混凝土高效外加剂质量符合《中华人民共和国国家标准 GB8076-2019 混凝土外加剂》规范、

《中华人民共和国建材行业标准 JC473-2001 混凝土泵送剂》标准要求、符合《中华人民共和国建材行业标

准 JC474-2008 砂浆、混凝土防水剂》标准要求。

FDT 系列混凝土高效外加剂在成都市机场路高架桥建设、泵送商品砼施工、油田大型设备基础及贮池砼施

工、高等级砼路面施工、水电站砼施工、重庆地区特细砂砼施工、铁路桥梁砼施工，以及我国南方炎热气候条

件下的砼施工中已得到大面积的应用。

FDT 系列混凝土高效外加剂属于非荼系、非引气型，适用于配制高强混凝土、泵送混凝土、大流动性混凝土、

自密实混凝土、喷射混凝土及预制构件混凝土等。

FDT 系列混凝土高效外加剂对各种类型的水泥有很好的适应性 , 配伍性好。

初次使用 FDT 系列混凝土高效外加剂或更换水泥品种时，先做必要的混凝土试配试验，以获得最佳效果。

FDT series concrete high-efficiency admixtures are new efficient admixtures, which have passed the review of

Sichuan Provincial Construction Committee, and obtained the \"License for Promotion of New Products and New

Technologies for Construction System in Sichuan Province\" (Certificate No.: 98016).

The quality of FDT series concrete high-efficiency admixtures meets the requirements of the National Standard of

the People's Republic of China (GB8076-2019 Concrete admixtures), the building materials industry standard of the

People's Republic of China (JC473-2001 Pumping aid for concrete), and the building materials industry standard of the

People's Republic of China (JC474-2008 Water-repellent admixture for mortar and concrete).

FDT series concrete high-efficiency admixtures have been widely used in the construction of Airport Road viaduct

in Chengdu, the construction of pumped commercial concrete, the construction of large equipment foundation and

storage tank in oilfields, the construction of high-grade concrete pavement, the construction of hydropower station, the

construction of ultra-fine sand concrete in Chongqing, the construction of railway bridge concrete, and the construction

of concrete under hot climate conditions in South China.

FDT series concrete high-efficiency admixtures belong to non-naphthalene and non-entraining type, and are

suitable for the preparation of high-strength concrete, pumped concrete, large flow concrete, self-compacting concrete,

shotcrete and precast member concrete, etc.

FDT series concrete high-efficiency admixtures have good adaptability to various types of cement and good

compatibility.

When using FDT series concrete high-efficiency admixtures for the first time or replacing cement type, necessary

concrete test shall be conducted first to obtain the best results.

Function features:

功能特点：

76 E 混凝土外加剂 Concrete admixtures

FDT 系列混凝土高效外加剂分类：

The classification of FDT series concrete high-efficiency admixtures:

产品名称

FDT-1

高效减水剂

FDT-2

高效减水剂

FDT-3

高效减水剂

FDT-4

早强高效减水剂

FDT-30

混凝土泵送剂

FDT-40

混凝土泵送剂

FDT-S

砂浆、混凝土防水剂

标准型

轻度缓凝型

缓凝型

早强型

缓凝型

轻度缓凝型

有机硅防水材料

HPWR-S

HPWR-R

HPWR-R

HPWR-A

PA

PA

0.4 ～ 1.0%

0.5 ～ 1.0%

0.5 ～ 1.0%

0.5 ～ 1.0%

0.5 ～ 1.0%

0.5 ～ 1.5%

配防渗混凝土 2.0 ～ 3.0%

建筑表面喷涂 30 ～ 40m/kg 2

特点 推荐掺量

Product name

FDT-1 High range water

reducing admixture

FDT-2 High range water

reducing admixture

FDT-3 High range water

reducing admixture

FDT-4 Hardening accelerating

type high range water

reducing admixture

FDT-30 Pumping admixture

of concrete

FDT-40 Pumping admixture

of concrete

FDT-S Water-repellent

admixture for mortar

and concrete

Standard type

Mild-retarding type

Set retarding type

Hardening

accelerating type

Set retarding type

Mild-retarding

type

Organic silicon

waterproof material

For preparing

impervious concrete,

the dosage is 2.0~3.0%

For building surface

spraying, the dosage is

30~40m²/kg

Feature

类型代号

Type code Recommended dosage

77

E 混凝土外加剂 Concrete admixtures

FDT-1 高效减水剂

FDT-1 High range water reducing admixture

FDT-1 高效减水剂属非荼系、非引气型，适用于配制高强混凝土、泵送混凝土、大流动性混凝土、自密实

混凝土、喷射混凝土及预制构件混凝土等。

1.FDT-1 掺量为 0.4 ～ 1.0% 时，减水率可达 20 ～ 30%, 节灰率可达 15 ～ 30%, 对于改善混凝土的

和易性，减水、节灰效果显著；

2. 保水性好，泌水率比低于 20%;

3. 含气量低，小于 3%，为非引气型减水剂；

4. 对混凝土凝结时间无明显影响，属非缓凝型减水剂；

5. 抗压强度高。抗压强度比：1 天达 200% 以上，3 天达 170% 以上，7 天达 160% 以上，28 天达

140% 以上，故采用 FDT-1 对于混凝土增强有显著的效果，特别适用于配制高标号混凝土；

6.FDT-1 的硫酸盐含量很低，避免了硫酸盐对混凝土的不良影响，以及克服寒冷条件下硫酸钠结晶影响

施工的问题，充分发挥产品的效能具有重要作用；

7.FDT-1 基本不含氯离子，对钢筋无锈蚀；

8.FDT-1 为非萘系减水剂，对人体及环境无危害。

FDT-1 推荐掺量 0.4 ～ 1.0%, 最佳掺量为 0.75%。

FDT-1 可以采用三种掺入方式：

1.FDT-1 与水泥及其他材料一起加入搅拌机内混拌均匀；

2.FDT-1 预先溶于水后，再把水泥及其他材料掺入混拌均匀；

3.FDT-1 用后掺法，先混拌好混凝土，再掺入 FDT-1 混拌均匀。

FDT-1 High range water reducing admixture belongs to non-naphthalene and non-gas diversion type, and is

suitable for the preparation of high-strength concrete, pumped concrete, large flow concrete, self-compacting concrete,

shotcrete and precast member concrete, etc.

1. When the dosage of FDT-1 is 0.4~1.0%, the water reduction rate can reach 20~30%, and the ash saving rate

can reach 15~30%. It can greatly improve the peaceability, water reduction effect and ash saving effect of concrete;

2. It has good water-retaining property, and the bleeding rate is less than 20%;

3. Its gas content is lower than 3%, and it is a non-gas diversion water-reducing agent;

4. It has no obvious effect on the setting time of concrete, and is a non-retarding water-reducing agent;

5. High compressive strength. Compressive strength ratio: over 200% for 1 day, over 170% for 3 days, over 160%

for 7 days, over 140% for 28 days; therefore, FDT-1 has a significant effect on concrete reinforcement, and is especially

suitable for the preparation of high-grade concrete;

6. The sulfate content of FDT-1 is very low, which avoids the adverse effect of sulfate on concrete, and overcomes

the problem of sodium sulfate crystallization affecting construction under cold conditions, and plays an important role

in giving full play to the efficiency of the product.

7. FDT-1 does not contain chloride ion basically and is not corrosive to rebars;

8. FDT-1 is a non-naphthalene water-reducing agent, and has no harm to human body and environment.

Function features:

推荐加量：

功能特点：

78 E 混凝土外加剂 Concrete admixtures

Recommended dosage:

Product quality:

产品质量：

Product packaging:

产品包装：

技术指标 Technical indicator：

The recommended dosage of FDT-1 is 0.4~1.0%, and the optimal dosage is 0.75%.

FDT-1 can be added in three ways:

1.FDT-1, cement and other materials are added to the mixer and mixed evenly;

2.After FDT-1 is dissolved in water, cement and other materials are added and mixed evenly;

3.The concrete is mixed first, and then FDT-1 is added and mixed evenly.

The net weight of FDT-1 dry powder is 25kg/bag, the outer layer adopts 3-in-1 kraft paper composite bag or plastic

woven bag, and the inner layer adopts polyethylene film bag.

In line with the National Standard of the People's Republic of China (GB8076-2019 Concrete admixtures)

FDT-1 干粉净重 25kg/ 袋，采用外层三合一牛皮纸复合袋或塑料编织袋，内层聚乙烯薄膜袋。

符合《中华人民共和国国家标准 GB8076-2019 混凝土外加剂》规范。

外观

PH 值（5% 水溶液）

氯根含量，%

水分，%

8 ～ 10

≤ 1.0

≤ 2.0

≤ 12.0

指标

Index

项目

Item

Appearance

棕褐色粉末

Brown powder

PH value(5% aqueous solution)

Chlorides root content

硫酸盐含量（以 Na SO计），%

Sulfate content (calculated as Na₂SO4)

2 4

Moisture content

79

E 混凝土外加剂 Concrete admixtures

Function features:

推荐加量：

功能特点：

FDT-2 高效减水剂

FDT-2 High range water reducing admixture

FDT-2 高效减水剂属非荼系、非引气型，适用于配制高强混凝土、泵送混凝土、大流动性混凝土、自密实

混凝土、喷射混凝土及预制构件混凝土等。

1.FDT-2 掺量为 0.5 ～ 1.0% 时，减水率可达 20 ～ 30%, 节灰率可达 15 ～ 30%, 对于改善混凝土的

和易性，减水、节灰效果显著；

2. 保水性好，泌水率比低于 20%;

3. 含气量低，小于 3%，为非引气型减水剂；

4. 对混凝土凝结时间略有延长，属轻度缓凝型减水剂；

5. 抗压强度高。抗压强度比：1 天达 160% 以上，3 天达 150% 以上，7 天达 140% 以上，28 天达

130% 以上，故采用 FDT-2 对于混凝土增强有显著的效果，特别适用于配制高标号混凝土；

6.FDT-2 基本不含氯离子，对钢筋无锈蚀；

7.FDT-2 为非萘系减水剂，对人体及环境无危害。

FDT-2 推荐掺量 0.5 ～ 1.0%, 最佳掺量为 0.8%。

FDT-2 可以采用三种掺入方式：

1.FDT-2 与水泥及其他材料一起加入搅拌机内混拌均匀；

2.FDT-2 预先溶于水后，再把水泥及其他材料掺入混拌均匀；

3.FDT-2 用后掺法，先混拌好混凝土，再掺入 FDT-2 混拌均匀。

FDT-2 High range water reducing admixture belongs to non-naphthalene and non-gas diversion type, and is

suitable for the preparation of high-strength concrete, pumped concrete, large flow concrete, self-compacting concrete,

shotcrete and precast member concrete, etc.

1. When the dosage of FDT-2 is 0.5~1.0%, the water reduction rate can reach 20~30%, and the ash saving rate

can reach 15~30%. It can greatly improve the peaceability, water reduction effect and ash saving effect of concrete.

2. It has good water-retaining property, and the bleeding rate is less than 20%;

3. Its gas content is lower than 3%, and it is a non-gas diversion water-reducing agent;

4. It can prolong the setting time of concrete slightly, and is a mild-retarding water-reducing agent;

5. High compressive strength. Compressive strength ratio: over 160% for 1 day, over 150% for 3 days, over 140%

for 7 days, over 130% for 28 days; therefore, FDT-2 has a significant effect on concrete reinforcement, and is especially

suitable for the preparation of high-grade concrete;

6. FDT-2 does not contain chloride ion basically and is not corrosive to rebars;

7. FDT-2 is a non-naphthalene water-reducing agent, and has no harm to human body and environment.

80 E 混凝土外加剂 Concrete admixtures

Recommended dosage:

The recommended dosage of FDT-2 is 0.5~1.0%, and the optimal dosage is 0.8%.

FDT-2 can be added in three ways:

1.FDT-2, cement and other materials are added to the mixer and mixed evenly;

2.After FDT-2 is dissolved in water, cement and other materials are added and mixed evenly;

3.The concrete is mixed first, and then FDT-2 is added and mixed evenly.

Product quality:

产品质量：

Product packaging:

产品包装：

FDT-2 干粉净重 25kg/ 袋，采用外层三合一牛皮纸复合袋或塑料编织袋，内层聚乙烯薄膜袋。

符合《中华人民共和国国家标准 GB8076-2019 混凝土外加剂》规范。

The net weight of FDT-2 dry powder is 25kg/bag, the outer layer adopts 3-in-1 kraft paper composite bag or plastic

woven bag, and the inner layer adopts polyethylene film bag.

In line with the National Standard of the People's Republic of China (GB8076-2019 Concrete admixtures)

技术指标 Technical indicator：

8 ～ 10

≤ 1.0

≤ 12.0

指标

Index

项目

Item

外观

Appearance

棕褐色粉末

Brown powder

PH 值（5% 水溶液）

PH value(5% aqueous solution)

氯根含量，%

Chlorides root content

水分，%

Moisture content

81

E 混凝土外加剂 Concrete admixtures

Function features:

功能特点：

FDT-3 高效减水剂

FDT-3 High range water reducing admixture

FDT-3 高效减水剂属非荼系、非引气型，适用于配制高强混凝土、泵送混凝土、大流动性混凝土、自密实

混凝土、商品混凝土、喷射混凝土及预制构件混凝土等。

1.FDT-3 掺量为 0.5 ～ 1.0% 时，减水率可达 20 ～ 30%, 节灰率可达 15 ～ 30%, 对于改善混凝土的

和易性，减水、节灰效果显著；

2. 保水性好，泌水率比低于 20%;

3. 含气量低，小于 3%，为非引气型减水剂；

4. 对混凝土凝结时间有延缓作用，属缓凝型减水剂；

5. 抗压强度高。抗压强度比：3 天达 150% 以上，7 天达 140% 以上，28 天达 130% 以上，故采用

FDT-3 对于混凝土增强有显著的效果，特别适用于配制高标号混凝土；

6.FDT-3 具有良好的抗高温性能，能满足炎热气候条件下施工的要求。

7. 在相同水灰比情况下，掺有 FDT-3 的混凝土可使坍落度提高 4 倍左右，且坍落度损失小，有利于解决

集中搅拌、长距离运输等作业问题；

8.FDT-3 基本不含氯离子，对钢筋无锈蚀；

9.FDT-3 为非萘系减水剂，对人体及环境无危害。

FDT-3 High range water reducing admixture belongs to non-naphthalene and non-gas diversion type, and is

suitable for the preparation of high-strength concrete, pumped concrete, large flow concrete, self-compacting concrete,

commercial concrete, shotcrete and precast member concrete, etc.

1.When the dosage of FDT-3 is 0.5~1.0%, the water reduction rate can reach 20~30%, and the ash saving rate can

reach 15~30%. It can greatly improve the peaceability, water reduction effect and ash saving effect of concrete.

2.It has good water-retaining property, and the bleeding rate is less than 20%;

3.Its gas content is lower than 3%, and it is a non-gas diversion water-reducing agent;

4.It can prolong the setting time of concrete, and is a retarding water-reducing agent;

5.High compressive strength. Compressive strength ratio: over 150% for 3 days, over 140% for 7 days, over

130% for 28 days; therefore, FDT-3 has a significant effect on concrete reinforcement, and is especially suitable for the

preparation of high-grade concrete;

6.FDT-3 has good resistance to high temperature and can meet the requirements of construction under hot weather

conditions.

7.Under the same water-cement ratio, the slump of concrete mixed with FDT-3 can be increased by about 4 times,

and the slump loss is small, which is conducive to solving the operation problems of centralized mixing and longdistance transportation;

8. FDT-3 does not contain chloride ion basically and is not corrosive to rebars;

9. FDT-3 is a non-naphthalene water-reducing agent, and has no harm to human body and environment.

82 E 混凝土外加剂 Concrete admixtures

Recommended dosage:

推荐加量：

FDT-3 推荐掺量 0.5 ～ 1.0%, 最佳掺量为 0.75%。

FDT-3 可以采用三种掺入方式：

1.FDT-3 与水泥及其他材料一起加入搅拌机内混拌均匀；

2.FDT-3 预先溶于水后，再把水泥及其他材料掺入混拌均匀；

3.FDT-3 用后掺法，先混拌好混凝土，再掺入 FDT-3 混拌均匀。

FDT-3 干粉净重 25kg/ 袋，采用外层三合一牛皮纸复合袋或塑料编织袋，内层聚乙烯薄膜袋。

符合《中华人民共和国国家标准 GB8076-2019 混凝土外加剂》规范。

The recommended dosage of FDT-3 is 0.5~1.0%, and the optimal dosage is 0.75%.

FDT-3 can be added in three ways:

1.FDT-3, cement and other materials are added to the mixer and mixed evenly;

2.After FDT-3 is dissolved in water, cement and other materials are added and mixed evenly;

3.The concrete is mixed first, and then FDT-3 is added and mixed evenly.

The net weight of FDT-3 dry powder is 25kg/bag, the outer layer adopts 3-in-1 kraft paper composite bag or plastic

woven bag, and the inner layer adopts polyethylene film bag.

In line with the National Standard of the People's Republic of China (GB8076-2019 Concrete admixtures)

Product quality:

产品质量：

Product packaging:

产品包装：

技术指标 Technical indicator：

6～9

≤ 1.0

≤ 12.0

指标

Index

项目

Item

外观

Appearance

棕黄色粉末

Brown yellow powder

PH 值（5% 水溶液）

PH value(5% aqueous solution)

氯根含量，%

Chlorides root content

水分，%

Moisture content

83

E 混凝土外加剂 Concrete admixtures

推荐加量：

FDT-4 推荐掺量 0.5 ～ 1.0%, 最佳掺量为 0.75%。

FDT-4 可以采用三种掺入方式：

1.FDT-4 与水泥及其他材料一起加入搅拌机内混拌均匀；

2.FDT-4 预先溶于水后，再把水泥及其他材料掺入混拌均匀；

3.FDT-4 用后掺法，先混拌好混凝土，再掺入 FDT-4 混拌均匀。

FDT-4 早强高效减水剂属非荼系、非引气、早强型，早强增强效果显著，特别适用于配制现浇混凝土、道

桥混凝土及预制构件混凝土等。使用 FDT-4可以打打缩短拆模时间，加快模板周转和施工进度，提高劳动生产率。

1.FDT-4 掺量为 0.5 ～ 1.0% 时，减水率可达 20% 以上 , 节灰率可达 15 ～ 30%, 对于改善混凝土的

和易性，减水、节灰效果显著；

2. 保水性好，泌水率比低于 20%;

3. 含气量低，小于 3%，为非引气型减水剂；

4. 对混凝土凝结时间无明显影响，但早强增强作用显著，属早强型减水剂；

5.抗压强度高。抗压强度比：1天达 170%以上，3天达 150%以上，7天达 140%以上 ,28天达 130%以上，

故采用 FDT-4 对于混凝土增强有显著的效果，特别适用于配制高标号混凝土；

6. 在相同水灰比情况下，掺有 FDT-4 的混凝土可使坍落度提高 4 倍左右，且坍落度损失小；

7.FDT-4 基本不含氯离子，对钢筋无锈蚀；

8.FDT-4 为非萘系减水剂，对人体及环境无危害。

FDT-4 Hardening accelerating type high range water reducing admixture belongs to non-naphthalene, nongas diversion and fast-hardening type, and is suitable for the preparation of cast-in-place concrete, road and bridge

concrete, precast member concrete, etc. FDT-4 can greatly shorten the stripping time, speed up the formwork turnover

and construction progress, and improve labor productivity.

1.When the dosage of FDT-4 is 0.5~1.0%, the water reduction rate can reach 20% or above, and the ash saving rate

can reach 15~30%. It can greatly improve the peaceability, water reduction effect and ash saving effect of concrete.

2.It has good water-retaining property, and the bleeding rate is less than 20%;

3.Its gas content is lower than 3%, and it is a non-gas diversion water-reducing agent;

4.It has no obvious effect on the setting time of concrete, but with significant fast-hardening effect, and is a fasthardening water-reducing agent;

5.High compressive strength. Compressive strength ratio: over 170%% for 1 day, over 150% for 3 days, over 140%

for 7 days, over 130% for 28 days; therefore, FDT-4 has a significant effect on concrete reinforcement, and is especially

suitable for the preparation of high-grade concrete;

6.Under the same water-cement ratio, the slump of concrete mixed with FDT-4 can be increased by about 4 times,

and the slump loss is small;

7.FDT-4 does not contain chloride ion basically and is not corrosive to rebars;

8.FDT-4 is a non-naphthalene water-reducing agent, and has no harm to human body and environment.

Function features:

功能特点：

FDT-4 早强高效减水剂

FDT-4 Hardening accelerating type high range water reducing admixture

84 E 混凝土外加剂 Concrete admixtures

Recommended dosage:

The recommended dosage of FDT-4 is 0.5~1.0%, and the optimal dosage is 0.75%.

FDT-4 can be added in three ways:

1.FDT-4, cement and other materials are added to the mixer and mixed evenly;

2.After FDT-4 is dissolved in water, cement and other materials are added and mixed evenly;

3.The concrete is mixed first, and then FDT-4 is added and mixed evenly.

The net weight of FDT-4 dry powder is 25kg/bag, the outer layer adopts 3-in-1 kraft paper composite bag or plastic

woven bag, and the inner layer adopts polyethylene film bag.

In line with the National Standard of the People's Republic of China (GB8076-2019 Concrete admixtures)

Product quality:

产品质量：

Product packaging:

产品包装：

FDT-4 干粉净重 25kg/ 袋，采用外层三合一牛皮纸复合袋或塑料编织袋，内层聚乙烯薄膜袋。

符合《中华人民共和国国家标准 GB8076-2019 混凝土外加剂》规范。

技术指标 Technical indicator：

6～9

≤ 1.0

≤ 12.0

指标

Index

项目

Item

外观

Appearance

棕黄色粉末

Brown yellow powder

PH 值（5% 水溶液）

PH value(5% aqueous solution)

氯根含量，%

Chlorides root content

水分，%

Moisture content

85

E 混凝土外加剂 Concrete admixtures

FDT-30混凝土泵送剂属非荼系、缓凝型高效泵送剂，适用于配制高强混凝土、泵送混凝土、大流动性混凝土、

自密实混凝土、商品混凝土、大体积混凝土及夏季施工混凝土等。

1.FDT-30 掺量为 0.5 ～ 1.0% 时，减水率可达 20 ～ 30%，节灰率可达 15 ～ 30%, 对于改善混凝土

的和易性，减水、节灰效果显著；

2. 保水性好，泌水率比低于 20%;

3. 含气量适当，小于 4.5%, 有超塑化的作用；

4. 对混凝土凝结时间有延缓作用，砼凝结时间 14 小时左右，属缓凝型泵送剂，也可以作为减水剂；

5. 抗压强度高。抗压强度比：3 天达 130% 以上，7 天达 125% 以上，28 天达 120% 以上，故采用

FDT-30 对于混凝土增强有显著的效果，特别适用于配制高标号混凝土；

6.FDT-30 具有良好的抗高温性能，能满足炎热气候条件下施工的要求；

7. 在相同水灰比情况下，掺有 FDT-30 的混凝土可使坍落度提高 4 倍左右，且坍落度损失小，3 小时坍

落度仍保持 200mm 以上，有利于解决集中搅拌、长距离运输等作业问题；

8.FDT-30 基本不含氯离子，对钢筋无锈蚀；

9.FDT-30 为非萘系泵送剂、减水剂，对人体及环境无危害。

FDT-30 Pumping admixture of concrete belongs to non-naphthalene and retarding type, and is suitable for the

preparation of high-strength concrete, pumped concrete, large flow concrete, self-compacting concrete, commercial

concrete, mass concrete, concrete for construction in summer, etc.

1.When the dosage of FDT-30 is 0.5~1.0%, the water reduction rate can reach 20~30%, and the ash saving rate can

reach 15~30%. It can greatly improve the peaceability, water reduction effect and ash saving effect of concrete.

2.It has good water-retaining property, and the bleeding rate is less than 20%;

3.Its gas content is appropriate, i.e. less than 4.5%, and it has the superplasticizing effect;

4.It can prolong the setting time of concrete to about 14 hours; it is a retarding-type pumping agent and can also

be used as efficient water-reducing agent;

5.High compressive strength. Compressive strength ratio: over 130% for 3 days, over 125% for 7 days, over 120%

for 28 days; therefore, FDT-30 has a significant effect on concrete reinforcement, and is especially suitable for the

preparation of high-grade concrete;

6.FDT-30 has good resistance to high temperature and can meet the requirements of construction under hot

weather conditions;

7.Under the same water-cement ratio, the slump of concrete mixed with FDT-30 can be increased by about 4 times,

the slump loss is small, and the slump remains above 200mm in 3 hours, which is conducive to solving the operation

problems of centralized mixing and long-distance transportation;

8.FDT-30 does not contain chloride ion basically and is not corrosive to rebars;

9.FDT-30 is a non-naphthalene series pumping agent and water-reducing agent, and has no harm to human body

and environment.

Function features:

功能特点：

FDT-30 混凝土泵送剂

FDT-30 Pumping admixture of concrete

86 E 混凝土外加剂 Concrete admixtures

推荐加量：

FDT-30 推荐掺量 0.5 ～ 1.0%, 最佳掺量为 0.75%。

FDT-30 可以采用三种掺入方式：

1.FDT-30 与水泥及其他材料一起加入搅拌机内混拌均匀；

2.FDT-30 预先溶于水后，再把水泥及其他材料掺入混拌均匀；

3.FDT-30 用后掺法，先混拌好混凝土，再掺入 FDT-4 混拌均匀。

FDT-30 干粉净重 25kg/ 袋，采用外层三合一牛皮纸复合袋或塑料编织袋，内层聚乙烯薄膜袋。

符合《中华人民共和国建材行业标准 JC473-2001 混凝土泵送剂》标准要求。

The recommended dosage of FDT-30 is 0.5~1.0%, and the optimal dosage is 0.75%.

FDT-30 can be added in three ways:

1.FDT-30, cement and other materials are added to the mixer and mixed evenly;

2.After FDT-30 is dissolved in water, cement and other materials are added and mixed evenly;

3.The concrete is mixed first, and then FDT-30 is added and mixed evenly.

The net weight of FDT-30dry powder is 25kg/bag, the outer layer adopts 3-in-1 kraft paper composite bag or

plastic woven bag, and the inner layer adopts polyethylene film bag.

In line with the building materials industry standard of the People's Republic of China (JC473-2001 Pumping aid

for concrete)

Recommended dosage:

Product quality:

产品质量：

Product packaging:

产品包装：

技术指标 Technical indicator：

6～9

≤ 1.0

≤ 12.0

指标

Index

项目

Item

外观

Appearance

棕黄色粉末

Brown yellow powder

PH 值（5% 水溶液）

PH value(5% aqueous solution)

氯根含量，%

Chlorides root content

水分，%

Moisture content

87

E 混凝土外加剂 Concrete admixtures

推荐加量：

FDT-40 混凝土泵送剂属非荼系、轻度缓凝型高效泵送剂，适用于配制高强度泵送混凝土、大流动性混凝土、

自密实混凝土，也可用于建筑、道路施工混凝土等。

1.FDT-40 掺量为 0.5 ～ 1.5% 时，减水率可达 12 ～ 20%，节灰率可达 10 ～ 20%, 对于改善混凝土

的和易性，减水、节灰效果显著；

2. 保水性好，泌水率比低于 20%;

3. 对混凝土凝结时间略有延长，属于轻度缓凝型泵送剂。掺量较低时也可以作为混凝土减水剂使用，有早

强作用；

4. 抗压强度高。抗压强度比：3 天达 120% 以上，7 天达 130% 以上，28 天达 120% 以上，故采用

FDT-40 对于混凝土增强有显著的效果；

5. 显著改善混凝土的泵送施工性能，在相同的水泥用量及水灰比条件下掺 FDT-40 的混凝土坍落度可提

高 100 ～ 200mm。3 小时内混凝土坍落度损失小；

6.FDT-40 基本不含氯离子，对钢筋无锈蚀；

7.FDT-40 为非萘系泵送剂、减水剂，对人体及环境无危害。

FDT-40 推荐掺量 0.5 ～ 1.5%：

1. 用作泵送剂时，推荐掺量为 0.75 ～ 1.2%；

2. 用作道路施工砼减水剂时 , 推荐掺量 0.5 ～ 0.6%。

FDT-40 Pumping admixture of concrete belongs to non-naphthalene and mild-retarding type, and is suitable for

the preparation of high-strength concrete, large flow concrete, self-compacting concrete; it can also be used in concrete

for building and road construction, etc.

1. When the dosage of FDT-40 is 0.5~1.5%, the water reduction rate can reach 12~20%, and the ash saving rate

can reach 10~20%. It can greatly improve the peaceability, water reduction effect and ash saving effect of concrete.

2. It has good water-retaining property, and the bleeding rate is less than 20%;

3. It can prolong the setting time of concrete slightly, and is a mild-retarding pumping agent. Low dosage can also

be used as concrete efficient water-reducing agent, with fast--hardening effect;

4. High compressive strength. Compressive strength ratio: over 120% for 3 days, over 130% for 7 days, over

120% for 28 days; therefore, FDT-40 has a significant effect on concrete reinforcement;

5. It can significantly improve the pumping performance of concrete, and the slump of concrete mixed with FDT40 can be increased by 100~200mm under the same cement dosage and water-cement ratio. The concrete slump loss

within 3 hours is small;

6.FDT-40 does not contain chloride ion basically and is not corrosive to rebars;

7.FDT-40 is a non-naphthalene series pumping agent and water-reducing agent, and has no harm to human body

and environment.

Function features:

功能特点：

FDT-40 混凝土泵送剂

FDT-40 Pumping admixture of concrete

88 E 混凝土外加剂 Concrete admixtures

FDT-40 可以采用三种掺入方式：

1、FDT-40 与水泥及其他材料一起加入搅拌机内混拌均匀；

2、FDT-40 预先溶于水后，再把水泥及其他材料掺入混拌均匀；

3、FDT-40 用后掺法，先混拌好混凝土，再掺入 FDT-40 混拌均匀。

FDT-40 干粉净重 25kg/ 袋，采用外层三合一牛皮纸复合袋或塑料编织袋，内层聚乙烯薄膜袋。

符合《中华人民共和国建材行业标准 JC473-2001 混凝土泵送剂》标准要求。

The recommended dosage of FDT-40 is 0.5~1.5%：

1.When used as a pumping agent, the recommended dosage is 0.75-1.2%;

2.When used as a water-reducing agent for road construction concrete, the recommended dosage is 0.5-0.6%.

FDT-40 can be added in three ways:

1.FDT-40, cement and other materials are added to the mixer and mixed evenly;

2.After FDT-40 is dissolved in water, cement and other materials are added and mixed evenly;

3.The concrete is mixed first, and then FDT-40 is added and mixed evenly.

The net weight of FDT-30dry powder is 25kg/bag, the outer layer adopts 3-in-1 kraft paper composite bag or

plastic woven bag, and the inner layer adopts polyethylene film bag.

In line with the building materials industry standard of the People's Republic of China (JC473-2001 Pumping aid

for concrete)

Recommended dosage:

Product quality:

产品质量：

Product packaging:

产品包装：

技术指标 Technical indicator：

8～ 10

≤ 1.0

≤ 12.0

指标

Index

项目

Item

外观

Appearance

浅棕黄色粉末

Light brown yellow powder

PH 值（5% 水溶液）

PH value(5% aqueous solution)

氯根含量，%

Chlorides root content

水分，%

Moisture content

89

E 混凝土外加剂 Concrete admixtures

推荐加量：

FDT-S 砂浆、混凝土防水剂是一种新型防水剂，属有机硅防水材料。

FDT-S 可广泛应用于建筑物外墙饰面、屋顶、墙面、地下工程、隧道、桥梁、水库、库房、卫生间和厨房

等防水防渗透处理，FDT-S 也能作为混凝土、砖瓦、天然石料、石棉瓦、石膏、加气板等建筑材料的防水处理，

以及文物保护等方面。

1.FDT-S 具有无色、无毒、无污染、不挥发、不易燃，有良好的耐腐蚀性和耐候性等优点。

2.FDT-S 具有防水寿命长、适用范围广、施工简单、成本低、安全环保等特点。

3.FDT-S 与各种建筑材料形成无色、看不见的憎水膜，能高度渗入水泥结构物内部，堵塞空隙和毛细孔，

形成永久性密封防水层。因而能保护砖石、混凝土等建筑材料免受大气、雨水侵蚀，有效地防止水的渗透，起

到防水、防风化、防污染的作用，避免建筑材料生苔藓及混凝土内可溶性盐浸出， 并且不会损坏建筑材料的多

孔性和透气性，大大改善砖石、混凝土等建筑材料的性能，提高混凝土的抗压强度和硬度，延长建筑物的寿命。

配防渗砂浆、混凝土用量 2.0 ～ 3.0%，建筑表面喷涂 30 ～ 40m /kg：

1. 按照质量比，将 1 份 FDT-S 加 9 ～ 11 份水混合均匀，制成防水材料，可用来配制防水砂浆、抹防水层；

2. 按照质量比，将 1 份 FDT-S 加 20 ～ 25 份水混合均匀，配成防水材料，再用于配制防渗混凝土。施

工方法与普通混凝土施工相同；

3. 按照质量比，将 1 份 FDT-S 加 2 ～ 3 份水混合均匀，配成防水材料，用于建筑物外表面处理。用喷雾

器喷涂或用刷子涂刷 2 ～ 3 遍即可。此种处理方法具有极佳的防水效果。

FDT-S Water-repellent admixture for mortar and concrete is a new water-proof agent,which belongs to organic

silicon waterproof material.

FDT-S can be widely used in water-proof and anti-seepage treatment for building exterior facade finish, roof, wall,

underground project, tunnel, bridge, reservoir, warehouse, toilet and kitchen; FDT-S can also be used in water-proof

treatment for concrete, brick and tile, natural stone, asbestos tile, gypsum, aerated plate and other building materials,

as well as for preservation of cultural relics.

1. FDT-S is colorless, non-toxic, non-polluting, non-volatile and non-flammable, and has the advantages of good

corrosion resistance and weather resistance.

2. FDT-S is featured by long water-proof life, wide application scope, simple construction, low cost, safety and

environmental protection, etc.

3. FDT-S can form a colorless, invisible hydrophobic film with various building materials, and can deeply

penetrate into the interior of the cement structure, blocking the voids and pores, and forming a permanent sealed

water-proof layer. Thus, it can protect masonry, concrete and other building materials from atmospheric and rain

erosion, effectively prevent water penetration, play a waterproof, anti-weathering, anti-pollution role, and avoid moss

on building materials and soluble salt leaching in concrete; besides, it will not damage the porosity and permeability

of building materials, and can greatly improve the performance of masonry, concrete and other building materials,

improve the compressive strength and hardness of concrete, and prolong the life of buildings.

Function features:

功能特点：

FDT-S 砂浆、混凝土防水剂

FDT-S Water-repellent admixture for mortar and concrete

2

90 E 混凝土外加剂 Concrete admixtures

Recommended dosage:

Product quality:

产品质量：

Product packaging:

产品包装：

For preparing impervious mortar and concrete, the dosage is 2.0~3.0%; for building surface spraying, the dosage

is 30~40m²/kg:

1. According to the mass ratio, 1 portion pf FDT-S and 9~11 portions of water are mixed evenly to make waterproof material, which can be used to prepare water-proof mortar and water-proof coating.

2. According to the mass ratio, 1 portion pf FDT-S and 20~25 portions of water are mixed evenly to make waterproof material, which is used to prepare impervious concrete. The construction method is the same as that of ordinary

concrete.

3. According to the mass ratio, 1 portion pf FDT-S and 2~3 portions of water are mixed evenly to make waterproof material, which is used for treatment of exterior surface of buildings. Only sprayer or brush is required for

spraying or brushing for 2~3 times. This treatment method has excellent water-proof effect.

FDT-S 液体净重 25kg/ 桶，采用高密度聚乙烯塑料桶包装；

符合《中华人民共和国建材行业标准 JC474-2008 砂浆、混凝土防水剂》标准要求。

The net weight of FDT-S liquid is 25kg/drum, and high-density polyethylene plastic drum is adopted.

In line with the building materials industry standard of the People's Republic of China (JC474-2008 waterrepellent admixture for mortar and concrete)

技术指标 Technical indicator：

水泥净浆流动度

≥ 32

≥ 3

≤ 18

1.23 ～ 1.25

≤ 1

指标

Index

项目

Item

外观

Appearance

浅黄色至无色透明液体

Light-yellow to colorless transparent liquid

大于基准水泥浆

Greater than benchmark cement slurry

含硅量，%

Silicon content

总碱量，%

Total alkali content

氯化钠含量，%

Sodium chloride content

Fluidity of cement paste

含固量，%

Solid content

密度，g/cm

Density

³

91

E混凝土外加剂 Concrete admixtures

部分检测设备

Partial inspection equipment

92 F 部分检测设备 Partial inspection equipment

2、公司注册商标横版

1、公司注册商标竖版

Horizontal version of company registered trademark

Vertical version of company registered trademark

公司注册商标

Registered trademark of the company

93

G 公司注册商标 Registered trademark of the company

公司实景图

Real picture of the company

94 H 公司实景图 Real picture of the company

95

H 公司实景图 Real picture of the company